High Quality Alusong Signage- Brush

颜色和表面

ALUSONG Brush aluminum composite panel is one of the special treatments used on the surface of the aluminum sheet.The surface aluminum skin is coating brush and anodized brush.The sheet can be finish in the color of silver and gold for your choice.The brushed finish range gives an alternative option to your facade cladding

Silver Sraight Brushed

Stainless Steel Brushed

产品范围

Aluminum alloy	AA1100 series
Aluminum skin	0.1mm,0.15mm,0.18mm,0.21mm,0.30mm,0.40mm,0.5mm
Panel thickness	2mm,3mm,4mm,5mm,6mm
Panel width	1220mm,1250mm,1500mm
Panel length	2440mm,3050mm,4050mm
Surface treatment	ANDONIZE BRUSHED
Glossy	20%-50%

Dimensional tolerance:

Panel width: ±2mm Panel length:±3mm

Panel thickness: ±0.2mm Panel diagonal: ≤5mm

Aluminum sheet thickness: ±0.01mm

产品属性

High resistance to peeling

Superior weather resistance

Light weight and easy to process

Coating evenness

Easy for maintenance

Impact resistance

产品应用

· Sign Making, Way finding

· Digital UV & Screen Printing

· Standoff Lettering

· Interior &exterior decoration

· Cladding&facade

· Modular Sign Systems

· Exhibition Design

· Outdoor Advertising

Application
Application
Application
Application
Application

技术数据

Description	Test standard	Polyester
Thickness of coating	Polyester paint >=16um	16um to 18um
Coating flexibility (T-bend)	Polyester paint≥3T	3T
Color different	ΔE≦2.0(follow color sample)	ΔE≦2.0
Pencil hardness	≧HB	≧2H
Chemical resistance	2%HCI or 2%NaOH test in 24 hours -No change	No change
Coating adhesion	≧1grade for 10810mm2gridding test	1grade
Resist solvent	100times with Dimethylebnzene without change	No change
Boiling water resistance	2 hours without change	No change
Peeling strength/stripping strength	Average ≧5N/mm of 180oc peel off for panel with 0.21mm alu.skin	5N/mm
Impact test for paint	20KG.cm impact-paint no split for panel	No split
Abrasion resistance (L/Mil)	NIL	NIL
Temperature resistance	-40℃ to +80℃ temperature without change of color difference and paint peel off,peeling strength average dropprate≦10%	Change of glossy only,no paint Peel off
Cofficient of linear Thermal Expansion	100℃ temperature difference	2.4mm/n
Detergent resistance (3%)	ASTM D2248	No change
Humidity Resistance (3000hrs,100%RH,100°F)	ASTM D2247	No change
Salt spray resistance (3000hrs,5% salt)	ASTM B117	No change
Resistance to Staining	600h radiate in 800W/M2 in humidity condition,glossiness deviation less grade 2,color difference ≦4.0	No change